SF-2Y Boundary Lubricated Lead-free Bearing

Boundary lubricated lead-free bearings are improved on the basis of SF-2. Its performance is the same as SF-2, but the surface does not contain lead, and the application field can be expanded to areas with environmental protection requirements. At present, this product has been used in imported textile equipment, plunger pump swing parts, automobile joystick parts and other medium-load, medium-speed, grease lubrication occasions.

Få et tilbud

PREV：SF-2S Lead-free Lubricated Bearing for Printing and Dyeing Machines NEXT：SF-2X Boundary Lubricated Bearing for Low-Speed Applications

produkt introduksjon
Parameter
Materialbeskrivelse
Kontakt oss

Produktfunksjoner

1 Kan arbeide lenge under oljefrie forhold.

2 Mer egnet for arbeidsforhold med lav hastighet og tung belastning, med god slitestyrke og ekstremt lav frikt.

3 Egnet for situasjoner hvor oljefilm er vanskelig å danne, som frem- og tilbakegående, roterende og intermitterende bevegelser.

4 Motstandsdyktig mot korrosjon og oksidasjon.

5 Vedlikeholdsfri og lang levetid.

Hvorfor velge oljefrie lagre

Reduser produksjonskostnadene

Det er ikke behov for oljetilførselsanordning, oljeinjeksjonshull eller olje groove-behandling, noe som i stor grad kan spare produksjonskostnader.

Reduser driftskostnadene

Det reduserer bruken av smøreolje betydelig, reduserer vedlikehold av utstyr, og unngår skjulte farer forårsaket av utilstrekkelig oljetilførsel, og reduserer effektivt driftskostnader.

Forkort designtiden

Den oljefrie designen forenkler produktstrukturen og sparer effektivt designtid. Vi er profesjonelle ODM Leverandører av SF-2Y Boundary Lubricated Lead-free Bearing

Bidrar til miljøvern

Det kreves ingen resirkulering av spillolje, noe som også er gunstig for miljøvernet.

Søknadsfelt

Høy temperatur

·Stålfabrikk

·Smelteovn

·Tørkeutstyr

· Bakeovn

· Varmekontroller

Vanntett

·Damport

·Vannpumpe

·Væskebryterstruktur

·Offshore strukturer

·Dokk- og siltmaskinutstyr

Kjemisk industri

· Kjemisk fabrikk

· Galvaniseringsutstyr

· Avløpsrenseutstyr

· Fargemaskineri

· Olje- og kjemisk raffineringsutstyr

Energi

·Vindkraft

·Ny energi

Skip

·Dekkskran

·Anker

·Lukedeksel

·Rorarm

·Løftemaskineri og løfteringutstyr

Bilproduksjon

·Stempelform

·Sveisestruktur

· Male- og tørkelinje

· Transportbånd av metall

·Maskinverktøy

Tung industri

· Maskiner for stålrørfabrikk

·Dekk- og papirfabrikker

·Kraftverk

· Tilkoblingsbryter for støpeinjeksjonsmaskineri

Konstruksjon, gruvedrift, lasting

·Blandere, kverner, pulveriseringsmaskiner

·Konstruksjons-maskineri

· Gruveutstyr

· Vevstangslagere

Bruer og heisskinner

·Brolager

·Bjelker, broer, hengebroer

· Kjernekraftreaktorer

·Damp-generator

Technical Parameters

Maximum bearing pressure: 70N/mm2
Applicable temperature range: -40~+130℃
Maximum sliding speed: 2.5m/s
Friction coefficient: 0.05~0.25
Maximum allowable PV value (dry): 2.8N/mm2 .m/s
Maximum allowable PV value (oil): 22N/mm2 .m/s

Metallographic Structure and Material Structure

①Polyoxymethylene and fiber mixture 0.3~0.5mm
②Spherical bronze powder 0.2~0.3mm
③Steel back 0.4~2.2mm
④Electroplated layer: Tin layer thickness 0.005mm or copper layer thickness 0.008mm

Application Features

Good load-bearing and wear-resistant performance.
Suitable for rotating motion and swinging motion under high load and low speed, and occasions where frequent opening and closing under load make it difficult to form fluid dynamic lubrication.
Under boundary lubrication conditions, it can be maintained without oiling for a long time, and oiling in the overlayer can make the bearing service life longer.
The surface plastic layer can leave a certain margin during processing and molding, and can be processed by itself after assembly and pressing into the seat hole to achieve better assembly size.
The product is mainly used in automobile chassis, metallurgical machinery, mining machinery, water conservancy machinery, construction machinery, agricultural machinery, rolling equipment, etc.
Because it does not contain lead, it can be widely used in lead-free fields.

Chemical Properties

Model	Air	Vacuum	Water	Steam	Weak acid	Medium acid	Strong acid	Alkaline solution
SF 2Y	good	good	good	good	poor	N/A	N/A	good

MMD-10 End Surface Friction and Wear Test

Model	Test Duration	Test Conditions			Friction Coefficient	Final Temperature	Final Wear Amount
Model	Test Duration	Lubrication Type	Speed	Pressure	Friction Coefficient	(℃)	(mm)
SF 2Y	3hr	Grease	0.4m/s	3.5N/mm2	0.088	53	0.01

Materialesammensetning og egenskaper
Material	CuZn25Al5Mn3Fe3	CuSn5Pb5Zn5	CuAl10Ni5Fe5	CuSn12	CuZn25Al5Mn4Fe3
Tetthet	8.0	8.9	7.8	8.9	8.0
Hardhet HB	>210	>70	>150	>95	>250
Strekkfasthet N/mm²	>750	>200	>600	>260	>800
Flyttestyrke N/mm²	>450	>90	>260	>150	>450
Forlengelse%	>12	>15	>10	>৪	>800
Koeffisient for lineær ekspansjon 10 ^-5 /℃	1.9	1.8	1.6	1.8	1.9
Begrense temperatur ℃	-40~300	-40~400	-40~400	-40~400	-40~150
Maks. Last N/mm²	100	60	50	70	120
Maks. Hastighet (Tørr) m/min	15	10	20	10	15
Maks.PV N/mm²*m/min	200	60	60	80	200
Komprimering av permanent deformasjon 300N/mm²	<0,01	<0,05	<0,04	<0,05	<0,05
*Stor etterspørsel med spesielle materialer er tilgjengelig.

Base Material Interchange
Materialkoder	Kina merkevarer GB1176-87	Internasjonal ISO 1338	Tyskland DIN	Japan JIS	Amerika ASTM(UNS)	England BS	Italia JM	Gjeldende betingelser
JDB støpt bronse	ZCuZn25AI5 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	Høy belastning, lav hastighet Vanlig brukt
JDB-1 Bronse	ZCuSn5 Pb5Zn5	GCuPb5 Sn5Zn5	DIN1705 G-CuSn5ZnPb	H5111 BC6	B30-92 C83600	LG2	JM7-15	Mellomlast, lav hastighet Vanlig brukt
JDB-2 Bronse	ZCuAI9Fe4 Ni4Mn2	GCuAI10 FeNiS	DIN17656 G-CuAI10Ni	H5114 AIBC3	B30-92 C95500	AB2	JM3-15	Mellomlast, middels hastighet, Vanlig brukt
JDB-3 Bronse	ZCuSn12		G-CuSn12	CAC503B	B30-92 C90800	PB2	JM1-15	Mellomlast, lav hastighet, Vanlig brukt
JDB-5	ZCuZn25AI6 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	Over høy belastning, lav hastighet, Høy belastning brukt

Solid smøremiddel
Smøremiddel	Egenskaper	Typisk bruk
SL1 Legg til grafitt	Utmerket motstand mot kjemikalier angrep og lav friksjon, temperaturgrense 400 ℃	Passer til generelle maskiner og under atmosfæren
SL4 PTFE tillegg	Laveste friksjon og god vannsmøring, temperaturgrense 300 ℃	Skip, hydraulisk turbin, gassturbin, etc.

SUBMIT

Om oss

Zhejiang Mingxu Machinery Manufacturing Co., Ltd. tidligere kjent som Jiashan Mingxu Precision Machinery Factory, ble grunnlagt i 2011. Selskapet er lokalisert i innlandet til Yangtze River Delta Integrated Development Demonstration Zone, med beliggenhet og praktisk transport. Med mer enn ti års produksjons- og FoU-erfaring har selskapet vært dypt involvert i utvikling og produksjon av solide smørelager, skateboards, glidebaner og glidere. ODM Leverandører og selskap av JFB skulderbussing flens grafitt innlagt selvsmørende lager i Kina. Produktproduksjonen tar i bruk moderne automasjonsutstyr, implementerer strengt ISO2000 kvalitetsstyringssystemstandarden, og hovedprosessene behandles av høypresisjons CNC-maskiner. Selskapets hovedprodukter dekker en serie produkter som JDB solide innlagte selvsmørende lagre, stål-kobber sintrede lagre, SF-1 selvsmørende lagre, SF-2 grense selvsmørende lagre og FB090 kobber lagre. Mye brukt i bilindustrien, anleggsmaskiner, metallurgisk utstyr, gruvemaskiner, sprøytestøping, mugg, tekstil, trykking og mange andre maskineri produksjonsfelt; Til nå har selskapets produkter spredt seg over hele Kina og eksportert til mange fremmede land, og er dypt anerkjent og elsket av innenlandske og utenlandske kunder. Mingxu Machinery følger tjenesteprinsippet om "kvalitetsorientert service av høy kvalitet", og streber etter å gi kundene profesjonelle produkter og tjenester. Supply Engros MXB-JFB Skulderbussing Flens Grafitt innlagt selvsmørende lager. Selskapet vil fortsette å introdusere talenter, forbedre styringsmekanismen, integriteten, utviklingen, innovasjonen og strebe etter å bygge en merkevare i verdensklasse.